Home  >  Journal list  >  MATERIALS TRANSACTIONS  >  Vol.49  No.6 (2008)  >  pp.1446-1450

MATERIALS TRANSACTIONS
<<Previous article Vol.49  No.6 (2008)   pp.1446 - 1450 Next article>>

Annealing of Amorphous Sm5Fe17 Melt-Spun Ribbon

Tetsuji Saito1)
1) Department of Mechanical Science and Engineering, Chiba Institute of Technology

An amorphous Sm5Fe17 melt-spun ribbon was annealed under various conditions to obtain the metastable Sm5Fe17 phase. The Sm5Fe17 phase could be obtained by annealing at temperatures between 873 K and 973 K for 0.1–1 h. However, the annealed specimens contained other phases such as the SmFe2 and SmFe3 phases depending on the annealing conditions. It was found that the specimen annealed at 873 K for 1 h consisted mostly of the Sm5Fe17 phase. The Sm5Fe17 phase could also be obtained by annealing the amorphous Sm5Fe17 melt-spun ribbon at 1073 K for 0.1 h or 0.3 h, but annealing at that temperature for 1 h resulted in decomposition of the metastable Sm5Fe17 phase and formed the equilibrium Sm2Fe17 and SmFe3 phases.


Keyword:
samarium-iron alloys, melt-spinning, amorphous alloys, magnetic properties

Received: October 16, 2007
Accepted: March 04, 2008 , Published online: May 25, 2008
Copyright (c) 2008 The Japan Institute of Metals