Journal of the Ceramic Society of Japan
<<Previous article Vol.118  No.1381 (September) (2010)   pp.792 - 798 Next article>>

Effect of B2O3 content on crack initiation under Vickers indentation test

Yoshinari KATO1)2), Hiroki YAMAZAKI1), Yoshihiro KUBO2), Satoshi YOSHIDA2), Jun MATSUOKA2) and Tomoko AKAI3)
1) Technical Division, Nippon Electric Glass Co., Ltd.
2) School of Engineering, The University of Shiga Prefecture
3) Research institute for Innovation in Sustainable Chemistry, National Institute of Advanced Industrial Science and Technology (AIST)


  Effect of B2O3 content on crack resistance was investigated by indentation tests of glass samples with various compositions of B2O3. The ternary SiO2–B2O3–Na2O glass system (SBN series) and non-alkaline aluminoborosilicate glass system (SAB series). When B2O3 is substituted with SiO2 in the SBN system (“SBN1” series), crack resistance has a relationship with density. In a series of the SBN system where density did not change with B2O3 content (“SBN2” series), crack resistance decreased with increasing B2O3 content. On the other hand, crack resistance increased with increasing B2O3 content in the SAB series, where density did not change. According to the results of NMR measurement, boron in 4-cordination state ([4]B) increased in the SBN2 series while boron in 3-cordination state ([3]B) increased in the SAB series with increasing B2O3 content. Therefore, crack resistance increases with increasing [3]B and decreases with increasing [4]B. The difference in structure between [3]B and [4]B containing glasses leads to different effect on residual stress around the indentation, resulting in difference in crack resistance.


Keyword:
Oxide glass, Crack initiation, Indentation, B2O3

Received: March 25, 2010
Accepted: June 17, 2010 , Published online: September 01, 2010
Copyright (c) 2010 The Ceramic Society of Japan