Journal of the Ceramic Society of Japan
<<Previous article Vol.120  No.1397 (January) (2012)   pp.15 - 20 Next article>>

Characteristics of BaTiO3-coated Ag powders directly prepared by spray pyrolysis

You Na KO1), Jung Hyun KIM1) and Yun Chan KANG1)
1) Department of Chemical Engineering, Konkuk University

  Spherical BaTiO3-coated Ag powders with dense structures were directly prepared by spray pyrolysis. Ag powder with 1 wt % BaTiO3 has particles of 0.53 µm mean diameter. BaTiO3 had good properties for coating Ag powders: it decreased the sintering of the Ag powder at temperatures between 700 and 900°C. Complete melting of pure Ag powder, forming dense Ag thick film, occurred at 700°C. Whereas at this temperature, partial melting of the 1 wt % BaTiO3-coated Ag powder occurred, forming Ag thick film with a porous structure. The pure Ag thick film shrunk 45% at 900°C. However, the thick films formed from 1 and 5 wt % BaTiO3-coated Ag powder had respective shrinkages of 31 and 21%, respectively at 900°C. The sheet resistances of the Ag thick films formed from the 1 wt % BaTiO3-coated Ag powder were 7.54, 4.93 and 4.09 m Ω/sq at firing temperatures of 700, 800 and 900°C, respectively.


Keyword:
Spray pyrolysis, Ag powder, Barium titanate, Electrode material

Received: August 05, 2011
Accepted: October 12, 2011 , Published online: January 01, 2012