Preparation of barium titanate hollow particle by two-step chemical solution deposition

Tomoya OHNO1), Tomoyuki SUGIURA1), Shinji WATANABE1), Hisao SUZUKI2), Takeshi MATSUDA1)
1) Department of Materials Science, Kitami Institute of Technology 2) Graduate School of Science and Technology, Shizuoka University

Barium titanate (BTO) hollow particles were prepared using two-step chemical solution deposition with a template particle. Polystyrene (PSt) was selected as the template particle, and N-(hydroxymethyl)acrylamide (HMAm) was polymerized as a comonomer to generate the hydrophilic group on the PSt template particle surface. The BTO monophase was attained at [Ba]/[TiO2] = 1.0 using 350°C pre-annealed TiO2 precursor hollow particles. The obtained BTO particle was a hollow structure with shell thickness of approximately 45 nm. The surface area of the obtained BTO hollow particle was 12 m2/g, which was approximately twice as large as that of alkoxide-derived BTO particles created with the same annealing temperature.

Perovskite material, High surface area, Catalyst, Chemical solution deposition, Nanocoating