Bulk Glassy Fe-Ga-P-C-B Alloys with High Saturation Magnetization and Good Soft Magnetic Properties Synthesized by Fluxing Treatment and Copper Mold Casting

Baolong Shen1), Hisamichi Kimura1), Akihisa Inoue1) and Takao Mizushima2)
1) Institute for Materials Research, Tohoku University
2) Magnetic Application Department, Alps Electric Co. Ltd.


The effect of fluxing treatment on the glass-forming ability for the Fe75Ga5P12C4B4 glassy alloy was investigated. The fluxing treatment was found to be effective for the elimination of heterogeneous nucleation sites. The glass transition temperature (Tg), crystallization temperature (Tx), supercooled liquid region (ΔTx) and reduced glass transition temperature (TgTm) are all increased by fluxing treatment. The Tg, Tx, ΔTx and TgTm values for Fe75Ga5P12C4B4 glassy alloy are 731 K, 768 K, 37 K and 0.610 respectively before fluxing treatment, increase to 749 K, 805 K, 56 K and 0.625 respectively after fluxing treatment. Bulk glassy Fe75Ga5P12C4B4 alloy rods with high saturated magnetization (Is) of 1.27 T and good soft magnetic properties of 1.6 A/m for coercive force (Hc) were prepared with diameters range up to 2.5 mm by the copper mold casting method of fluxed alloy melt. The glass synthesis consists of preparing the alloy ingot by induction melting, thermal cycling and purifying the melt in B2O3 flux inside a silica tube and then casting the purified alloy into a copper mold. The size of 2.5 mm in diameter of the rod is not an upper limit.


Keyword:
fluxing treatment, bulk glassy alloy, high saturation magnetization, good soft magnetic properties, high reduced glass transition temperature

Received: October 11, 2000
Accepted: December 19, 2000 , Published online: September 06, 2005
Copyright (c) 2005 The Japan Institute of Metals

PDFPDF file (J-STAGE)J-STAGEJ-STAGE


SPARC Japan

Terms of Use | Privacy Policy