You are not logged in Total: 7journals, 19,556articles Online
AccountAccount
Login / Register
Forgot Login?
 
Main menuMain menu
What's new
Journal list
Visiting ranking
Phrase ranking
Polls
About us
 
SearchSearch
 
Journal Site
Advanced Search
 

Home  >  Journal list  >  Journal of the Ceramic Society of Japan ( 2003 - 2007 )  >  Vol.113  No.1314 (February) (2005)  >  pp.188-190

Journal of the Ceramic Society of Japan ( 2003 - 2007 )
<<Previous article Vol.113  No.1314 (February) (2005)   pp.188 - 190 Next article>>

Sintering and Mechanical Properties of AlZrC2

U. LEELA-ADISORN1), S.-M. CHOI1), Nobuyuki TERA1), Takeshi TAKEUCHI1), Shinobu HASHIMOTO1), Sawao HONDA1), Hideo AWAJI1), Kazuyuki HAYAKAWA2) and Akira YAMAGUCHI3)
1) Nagoya Institute of Technology
2) Japan Fine Ceramics Center
3) Okayama Ceramics Center


  AlZrC2 powder prepared by solid-state reaction was sintered using a pulse electric current sintering technique in a temperature range from 1700 to 2000°C under the pressure of 40 MPa in vacuum for 5 min. The density and mechanical properties of the sintered AlZrC2 monolith were estimated. As heating temperature increased, the density of the AlZrC2 monolith increased and the mechanical properties were improved. The bulk density of the AlZrC2 monolith sintered at 2000°C was 5.12 g/cm3. The maximum values of the fracture strength and Vickers' hardness were 380 MPa and 11.1 GPa, respectively.



Keyword:
Complex carbide, AlZrC2, PECS, Mechanical properties, Fracture strength, Vickers' hardness

Received: December 06, 2004
Accepted: December 10, 2004 , Published online: February 01, 2005
Copyright (c) 2005 The Ceramic Society of Japan

PDFPDF file (J-STAGE)J-STAGEJ-STAGE


SPARC Japan

Terms of Use | Privacy Policy