Home  >  Journal list  >  MATERIALS TRANSACTIONS  >  Vol.49  No.4 (2008)  >  pp.850-853

MATERIALS TRANSACTIONS
<<Previous article Vol.49  No.4 (2008)   pp.850 - 853 Next article>>

Effects of Aging Treatment on the Bending Strength in AZ91D/Al18B4O33w Composite

W. G. Wang1), W. L. Li2), K. C. Chang1), K. Matsugi1) and G. Sasaki1)
1) Department of Mechanical System Engineering, Graduate School of Engineering, Hiroshima University
2) Department of Mechanical Engineering, Tokushima University


Aluminum borate whisker (Al18B4O33w, denoted by ABOw) reinforced AZ91D (Mg-Al-Zn) magnesium alloy composites were prepared by squeeze casting. The composite was solution-treated at 683 K for 345.6 ks in argon atmosphere and then water-quenched. Aging treatment was carried out at 443 K in oil-bath. While the composite was cooled from the solution temperature of 683 K to room temperature, large thermal residual stress (TRS) was formed due to the mismatch of thermal expansion coefficient between ABOw and AZ91D matrix. The TRS of AZ91D matrix in as-quenched AZ91D/ABOw composite was measured with X-ray diffraction (XRD) and it was 103 MPa. After aging for 115.2 ks, the TRS relaxed and decreased to 45 MPa. Owing to the formation of precipitates, the bending strength of peak-aged composite (aged for 115.2 ks) was enhanced. Nevertheless, when the composite was aged for 345.6 ks, the bending strength decreased greatly. Even the bending strength of over-aged composite was lower than that of as-quenched composite. It is attribute to the coarsening of continuous precipitate within composite matrix close to whiskers.


Keyword:
AZ91D magnesium alloy, aluminum borate whisker, composite, bending strength, aging, thermal residual stress.

Received: December 03, 2007
Accepted: January 21, 2008 , Published online: March 25, 2008